| Failure Mechanism of Precast Defective Concrete Based on Image Statistics |
|
SUN Haokai1,2, GAO Yang3, ZHENG Xinyu1, CHEN Yibo4
|
|
1.Geotechnical and Structural Engineering Research Center, Shandong University, Jinan 250061, China;2.School of Qilu Transportation, Shandong University, Jinan 250002, China;3.Structure Health Monitoring and Control Institute, Shijiazhuang Tiedao University, Shijiazhuang 050043, China;4.Key Laboratory of Transportation Tunnel Engineering of Ministry of Education, Southwest Jiaotong University, Chengdu 610031, China
|
| Abstract: |
| The uniaxial loading failure process of precast defective concrete containing expanded polystyrene（EPS） particles was investigated by computed tomography（CT）， acoustic emission（AE） and digital image processing（DIP） modeling methods. The mechanism of internal defects on crack propagation was revealed by practical mesoscopic modeling methods. The results show that the cracks appear at the corner initially and the defect closer to the outside of the concrete. The bearing capacity is seriously affected by split-type cracks. The open cracks often appear at the largest macroscopic defect in the horizontal projection. The rationality of using expanded polystyrene particles as prefabricated defects in the concrete is confirmed by CT scan. The established model can accurately describe the mechanical behavior， which verifies the consistency of meso-simulation and mechanical experiment. |
| Key words: concrete defect computed tomography expanded polystyrene digital image processing |