| 摘要: |
| 基于48个标准拉拔试验，对芳纶纤维塑料(AFRP)筋与普通C50混凝土、高性能C50混凝土、环氧树脂和水泥浆之间的黏结强度进行了比较系统的研究.结果表明：AFRP筋试件的破坏模式分为拔出破坏和劈裂破坏2种；破坏模式对AFRP筋黏结强度的影响不大；AFRP筋与混凝土的黏结强度约为变形钢筋与混凝土黏结强度的0.79～1.11倍；相比于高性能C50混凝土，AFRP筋与普通C50混凝土的黏结强度高10%左右；AFRP筋与环氧树脂的黏结强度较高，而与水泥浆的黏结强度则较低.最后，对AFRP筋与混凝土黏结强度的计算方法进行了探讨. |
| 关键词: 芳纶纤维塑料筋 混凝土 黏结滑移（τ S）曲线 破坏模式 黏结强度 |
| DOI：10.3969/j.issn.1007 9629.2015.04.002 |
| 分类号: |
| 基金项目:教育部新世纪优秀人才支持计划项目（NCET 10 0636） |
|
| Bond Strength of AFRP Rebars in Concrete |
|
XUE Weichen, FANG Zhiqing, WANG Yuan, KANG Mingrui
|
|
College of Civil Engineering, Tongji University, Shanghai 200092, China
|
| Abstract: |
| Based on tests of 48 pull out specimens, bond properties of AFRP rebars in C50 normal strength concrete, C50 high performance concrete, epoxy resin and grout were systematically investigated. The test results showed that the modes of failure for pull out specimens with AFRP rebars included pull out failure and splitting failure. The failure mode did not significantly affect the bond strength of pull out specimens. The experiment also showed that the bond strength of AFRP rebars in concrete was 0.79 to 1.11 times that of the deformed steel rebars. The bond strength of AFRP rebars in normal strength concrete was about 10% higher than that in high performance concrete. Compared with the AFRP rebars in concrete, the bond strength was higher than that in epoxy resin but lower than that the grout. Generally, the bond strength of AFRP rebars decreases with the diameter increasing. In addition, the calculation methods for the bond strength of AFRP rebars in the concrete were discussed. |
| Key words: AFRP rebar concrete τ S curve failure mode bond strengt |