Interfacial Bonding Performance between Corrugated Steel Fiber and Hybrid Fiber Concrete Matrix
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    考虑钢聚丙烯混杂纤维体积分数、波纹型钢纤维埋置深度和混凝土基体强度等因素,设计制作了21组混杂纤维混凝土拉拔试件,通过拉拔试验研究了波纹型钢纤维与混杂纤维混凝土基体的界面黏结性能.基于实测的钢纤维拉拔力滑移曲线,分析了上述因素对波纹型钢纤维最大黏结力和拉拔功的影响规律,阐明了界面黏结机理.结果表明:当波纹型钢纤维体积分数为150%、聚丙烯纤维体积分数为005%时,界面黏结性能最佳;界面黏结力随着基体强度的提高而提高;增大钢纤维的埋置深度,界面黏结强度提高,但当埋置深度大于8mm时,界面黏结强度随着埋置深度的增加而减小.

    Abstract:

    21groups of steel polypropylene hybrid fiber concrete pull out specimens were designed to study the influences of hybrid fiber content, embedded depth and matrix strength on the interfacial bonding performance between corrugated steel fiber and hybrid fiber concrete matrix through one sided steel fiber pull out tests. The peak pull out force and pull out work were measured to analyze the influences of the aforementioned factors on the interfacial bonding performance between the corrugated fiber and the matrix. Moreover, the bonding mechanism of the fiber matrix interface was also revealed. Results show that the fiber pull out force reached maximum when the steel fiber content and polypropylene fiber content were kept to 150% and 005%, respectively. The interfacial bonding behavior can also be improved with the increase of concrete matrix strength. Increasing the fiber embedded depth is favorable to the increase of the pull out force. However, above the embedded depth greater than 8mm, the interfacial bonding strength gradually decreased with the increase of the embedded depth.

    参考文献
    相似文献
    引证文献
引用本文

王力,徐礼华,邓方茜,刘素梅,池寅.波纹型钢纤维混杂纤维混凝土界面黏结性能[J].建筑材料学报,2020,23(4):865-874

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-03-20
  • 最后修改日期:2019-08-10
  • 录用日期:
  • 在线发布日期: 2020-08-27
  • 出版日期: