Effect of Decalcification on CSH Gel Microstructure in Cement Paste
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用X射线荧光分析、X射线衍射、Fourier红外光谱、29Si固体核磁共振谱结合去卷积技术研究了脱钙对水泥(ASTMⅠ型)浆体中CSH凝胶结构的影响.结果表明:对于水化3,28d的水泥浆体,其脱钙过程均为2个阶段,即:当水泥浆体的钙硅比(摩尔比)由2.78左右降至2.00左右时,几乎全部游离的CH被脱去,CSH凝胶部分脱钙,浆体的脱钙主要在这个阶段完成,CSH平均链长分别由2.4,2.9增加至4.4,5.8,且I(Q2)/I(Q1)增加;当水泥浆体的钙硅比降至1.83左右时,CSH凝胶脱钙,并产生了更显著的聚合,CSH平均链长进一步分别增加至6.2,9.9,且I(Q2)/I(Q1)继续增加;Alite和Belite在整个脱钙过程中的变化并不明显.脱钙过程中CSH二聚体向更高聚合态转变,但是Al掺杂会影响CSH结构的稳定性.从分子尺度理解,脱钙如能使桥硅氧四面体结构稳定,对于CSH结构的优化是有利的

    Abstract:

    Effect of decalcification on microstructure of CSH gel in ASTMⅠcement paste were studied by Xray fluorescence spectrometer(XRF), Xray diffraction(XRD), infrared spectroscopy with Fourier transform(FTIR) and 29Si MAS NMR with deconvolution technique. It is shown from test results that the decalcification process can be divided into two stages. When the molar ratio of CaO to SiO2 in the pastes at 3, 28d is lowered from~2.78 to~2.00, almost all of CH is removed and CSH gel is partially decalcified, the average chain length(ACL) of CSH is increased from 2.4 to 4.4 for 3d paste and from 2.9 to 5.8 for 28d paste respectively, and I(Q2)/I(Q1) is also increased. While the molar ratio of CaO to SiO2 in the pastes comes to~1.83, decalcification of CSH gel occurs. CSH polymerizes and I(Q2)/I(Q1) increases largely in this stage, which results in further increase of ACL to 6.2 for 3d paste and 9.9 for 28d paste. The mechanism of increase of CSH polymerization could be transformation of dimeric CSH toward highly polymerized CSH. However, Al doping could affect the stability of CSH microstructure. In molecular level, the existence of the pure bridging siliconoxy tetrahedrons in CSH is beneficial to the optimization of the microstructure.

    参考文献
    相似文献
    引证文献
引用本文

何真,王磊,邵一心,蔡新华.脱钙对水泥浆体中CSH凝胶结构的影响[J].建筑材料学报,2011,(3):293-298

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2010-03-10
  • 最后修改日期:2010-06-17
  • 录用日期:
  • 在线发布日期:
  • 出版日期: