| 摘要: |
| 用粉煤灰等质量替代20%，30%，50%水泥后，将水泥石灰石粉粉煤灰净浆样品置于（5±2）℃的10%（质量分数）硫酸镁溶液中15个月，加速碳硫硅钙石型硫酸盐侵蚀（TSA）.对腐蚀产物进行了红外光谱定性分析和X射线衍射定量分析，通过灰色关联分析研究了粉煤灰对TSA的影响.结果表明：粉煤灰对水泥基材料的TSA影响与其组成、掺量及细度等因素有关；粉煤灰活性指数对碳硫硅钙石形成影响最大，可作为筛选粉煤灰预防TSA破坏的指标；活性指数大于80%的粉煤灰，其掺量达到50%时可显著改善水泥基材料的抗TSA性能. |
| 关键词: 碳硫硅钙石型硫酸盐侵蚀 粉煤灰 灰色关联分析 化学组成 掺量 |
| DOI：103969/j.issn1007 9629201404022 |
| 分类号: |
| 基金项目:国家重点基础研究发展计划（973计划）项目（2009CB623106） |
|
| Effects of Fly Ash on Thaumasite Form of Sulfate Attack |
|
LI Changcheng1, XU Zhenran2, CHEN Tongde2
|
|
1.State Key Laboratory of Green Building Materials, China Building Materials Academy, Beijing 100024, China;2.Department of Electrical Engineeting, Binzhou Technical College, Binzhou 256603, China
|
| Abstract: |
| Cement was equally replaced by fly ash with 20%, 30% and 50% proportions. Cement limestone fly ash paste samples were immerged in 10% magnesium sulfate solution(by mass) at (5±2)℃ for 15months to accelerate thaumasite form of sulfate attack(TSA). The corrosion products were qualitatively analyzed by infrared spectrum(IR) and quantitatively analyzed by X ray diffraction(XRD)/Rietveld refinement methods. The effect index of fly ash on TSA was investigated by gray correlation analysis. The results show that:effects of fly ash on TSA are closely related to the composition, content of fly ash. The activity index of fly ash has a maximum gray correlation degree to quantity of thuamasite formation which could be used as an index for filtering fly ash to prevent TSA. Fly ash with an activity index >80% could improve the resistance to TSA in cement based materials when the content reached 50%. |
| Key words: thaumasite formation of sulfate attack(TSA) fly ash gray correlation analysis chemical composition content |