| 研究了环氧树脂混凝土试件在自制微波辐射装置下的固化时间，发现其在该条件下10min即可实现基本固化，并达到较高强度；进一步研究了微波固化环氧树脂混凝土的力学性能，结果表明：该混凝土抗压强度近50MPa，抗折强度可达10MPa以上，且与原结构黏结强度高，同时具有良好的低温性能.研究用微波固化环氧树脂混凝土具有高强、快硬、施工方便及固化易于控制等优点，可应用于路面抢修抢建工程. |
| 关键词: 环氧树脂混凝土 微波固化 力学性能 路面抢修 |
| DOI：10.3969/j.issn.1007 9629.2013.04.008 |
| 分类号: |
| 基金项目:解放军总后勤部基建营房部项目（BY209C022）；重庆市建委科技项目（2009第92号） |
|
| Mechanical Performance of Repair Materials for EpoxyResin Concrete Pavement Cured by Microwave |
|
LEI Yun bo, JIANG Mao, CHEN Hui guo, ZHANG Li
|
|
Department of Military Civil Engineering, Logistical Engineering University, Chongqing 401331, China
|
| Abstract: |
| As the repair time of pavement is highly required, the curing time of epoxy resin concrete under the condition of self made microwave radiation equipment is tested. The results show the epoxy resin concrete can be cured in 10 minutes. The mechanical properties of cured resin concrete were studied and the results show that resin concrete cured by microwave has compressive strength of 50 MPa, flexural strength of above 10 MPa, and good low temperature deformation ability. The developed epoxy resin concrete has a lot of advantages, such as rapid hardening, high strength, convenient construction, which is suitable for rapid road repairing and constructing engineering. |
| Key words: epoxy resin concrete microwave curing mechanical performance pavement repair |