| 摘要: |
| 通过浸水试验及水中快速冻融试验,探讨分析了轻骨料含水率对混凝土吸水性及抗冻性的影响.结果表明,如果轻骨料含水率减小,则混凝土坍落度的经时损失率加大,混凝土抗压强度增高,吸水性降低;轻骨料混凝土的抗冻性由轻骨料含水率控制.本试验范围内,要满足含气量为5.5%(体积分数)的轻骨料混凝土抗冻性要求,则轻骨料含水率应控制在14 %～17%(质量分数)以下,而且设计水灰比越大,轻骨料的含水率就越有必要降低. |
| 关键词: 轻骨料 含水率 吸水性 抗冻性 |
| DOI： |
| 分类号:TU528.2 |
| 基金项目:教育部留学回国人员科研启动基金资助项目，黑龙江省博士后经费资助项目? |
|
| Effects of Water Content in Lightweight Aggregate on Water-Absorbing Property and Freeze-Thaw Resistance of Concrete |
|
MAO Ji-ze QI Hui AYUTA Ko-ichi
|
| Abstract: |
| According to water immersion tests and rapid freezing and thawing tests in water,the effects of water content in lightweight aggregate on water-absorbing property and freeze-thaw resistance of lightweight aggregate concrete were investigated.The results show that lightweight aggregate with lower water content absorbs more water in fresh concrete,which causes higher slump loss and decreases the actual water-cement ratio.Then the compressive strength of hardened concrete increases and the water-absorption dec... |
| Key words: lightweight aggregate water content water-absorbing property freeze-thaw resistance |