| 摘要: |
| 研究不同激发剂对以粉煤灰为原料制备的地聚合物抗压强度的影响．研究结果表明：不同浓度的NaOH和KOH溶液对粉煤灰的激发效果较差，粉煤灰基地聚合物的抗压强度较低．碱溶液和K2SiO3溶液复合可提高激发效果，提高粉煤灰基地聚合物的抗压强度．激发效果最好的是K2SiO3溶液；随着K2SiO3溶液浓度的提高，粉煤灰基地聚合物的抗压强度逐渐提高；当K2SiO3浓度为2mol／L时，粉煤灰基地聚合物28d抗压强度达到最大；继续增大K2SiO3浓度，粉煤灰基地聚合物28d抗压强度反而下降，由此可以推测相应的地聚合反应是一个定量的反应过程． |
| 关键词: 激发剂 粉煤灰 地聚合物 抗压强度 |
| DOI： |
| 分类号:TQ172.7 |
| 基金项目: |
|
| Effects of Activator on Compressive Strength of Fly Ash-Based Geopolymers |
|
HOU Yun-fen WANG Dong-min LI Qiao
|
| Abstract: |
| The effects of different activators on compressive strength of fly ash-based geopolymers were studied.It is shown that the activative effect of NaOH and KOH solution with different concentration is weak,the compressive strength of fly ash-based geopolymers is low,but the activative effect intensifies when NaOH or KOH solution mixes with K_2SiO_3 solution,and the compressive strength improves too.The K_2SiO_3 solution shows the best activative effect,the compressive strength of fly ash-based geopolymers increases with increasing concentration of K_2SiO_3 solution.When the solution concentration is 2 mol/L,the 28 d compressive strength reaches the maximum,then it decreases with the increase of the solution concentration.It is guessed that geopolymerization is a stoichiometric reaction. |
| Key words: activator,fly ash,geopolymers,compressive strength |