| 以废玻璃纤维硬丝为主要原料，添加适量外加剂，采用烧结法制备出质量符合要求的泡沫玻璃，并探讨了其发泡机理．研究认为发泡机理是：发泡剂放出的气体一部分由于烧结被包裹在坯体中形成微小气泡，当温度升高至发泡温度，玻璃软化时气泡膨胀，坯体体积增大而成为泡沫玻璃．引入适当配合的稳泡剂、加入结合剂并加压成型，能够促进烧结，这些对干气泡的形成和稳定都有积极作用。 |
| 关键词: 泡沫玻璃 废玻璃 发泡机理 气泡膨胀 制备 坯体 发泡剂 外加剂 纤维 稳泡剂 |
| DOI： |
| 分类号:TU528.2 TQ171.722 |
| 基金项目:盐城工学院青年科研基金资助项目 |
|
| Preparation of Foam Glass from Waste Stiff Glass-fiber |
|
CHEN Jian-hua LI Yu-hua LI Yu-shou
|
| Abstract: |
| Foam glass was prepared with sintered process, using moderate amount of additives and the powder of waste stiff glass fiber as main material and its foaming mechanism was investigated. Its foaming mechanism is that some gas given off from foaming agents, is confined and therefore many small bubbles are formed in the brick of foam glass due to sintering. Because of softening of the glass and expansion of the bubbles at foaming temperature, the glass block begins to enlarge and to form foam glass. Proper bubble stabilizers, binders and increasing pressure in the brick forming process make sintering speed up and be in favor of the formation and stabilization of the bubbles. |
| Key words: foamed glass stiff glass-fiber foaming mechanism |